Material: high strength low alloy steel
Grade: HC800LA
Thickness: 1.5/1.64mm
Forming technology: cold forming
Microalloyed steels have the advantages of simple composition design, low carbon equivalent, excellent weldability, excellent bendability and energy economy. It can be used to manufacture slide rails, structural parts and safety parts. Baosteel can commercially supply microalloy steel products with yield strength ranging from 500MPa to 850MPa. HC900LA has also been completed in industrial production with yield strength reaching 900MPa class and tensile strength≥980MPa.
Material: QE (QP steel with high hole expansion ratio) steel
Grade: HC650/980QE
Thickness: 2mm
Forming technology: cold forming for X-GPa®
QE980 is a new branch of BaoQP®. It combines high strength, high hole expansion ratio, medium elongation and better bendability. Its’s suitable for those parts with distinctive flanging and reaming features because of its excellent comprehensive formability.